120 Degree Heat Shrink Biaxially Oriented Polypropylene Plastic Film Use for Cigarette Packing

• Customization: Available
• Material: BOPP
• Type: Shrink Film
• Model NO.: BO059
• Transparency: Transparent
• Hardness: Soft
• Molding method: Blow Molding
• Length: 2000m-3000m
• Width: 120mm-550mm
• Thickness: 21-25micron
• Holographic: Available
• Shrinkage: 2%-10%
• Item Name: BOPP Film
• EVA: 24 Gloss
• Tensile Strength: 200
• Transport Package: Pallets / Carton Also Available
• Specification: 120mm
• Trademark: Binhao
• Origin: China
• HS Code: 3920209090
• Production Capacity: 300 Tons/Month

Product Description

120 Degree Heat Shrink Biaxially Oriented Polypropylene Plastic Film Use For Cigarette Packing


Introduction:
 

Production of BOPP film is made from polypropylene polymer melt through the long and narrow nose first sheet or thick film, and then within the special drawing machine, under certain temperature and the set speed, at the same time two or step by step in the vertical direction (vertical, horizontal) on the drawing, and through the appropriate cooling or heat treatment or special processing (such as corona, coating, etc.) made of thin film.

 

The abbreviation of BOPP is "Biaxially Oriented Polypropylene", BOPP film is two-way stretch Polypropylene film. Production of BOPP film is made from polypropylene polymer melt through the long and narrow nose first sheet or thick film, and then within the special drawing machine, under certain temperature and the set speed, at the same time two or step by step in the vertical direction (vertical, horizontal) on the drawing, and through the appropriate cooling or heat treatment or special processing (such as corona, coating, etc.) made of thin film.

 

Details:

 

NO.	Item			Unit	Index		Remarks
Size deviation
1	Width deviation	50~150		mm	±0.5		-
		151~400			±1.0		-
		401~1200			±1.5		-
2	Maximum thickness deviation	12~19μm		%	±5.0		-
		20~29μm			±4.0		-
		30~50μm			±3.0		-
Physical and mechanical properties
					Ordinary heat sealable film	Shrinkage heat sealable film	-
1	Tensile strength		Vertical	MPa	≥125	≥130	-
			Horizontal		≥220	≥240	-
2	Elongation at break		Vertical	%	≤200	≤200	-
			Horizontal		≤80	≤70	-
3	Hot-shrinkage rate		vertical	%	≤5.0	>5	-
			horizontal		≤4.0	>4	-
4	Young modulus		Vertical	MPa	1800	>2000	5mm/min
5	Haze			%	≤3.5	≤2.5	-
6	Coefficient			-	≤0.5	≤0.4	Single side
7	Ultimate strength			N/15mm	≥2.0	≥2.0	(135±5)ºC·0.18MPa·1s
8	Luster(45º)%			-	≥80	≥85	-
9	Wetting tension			mN/m	-	-	Conform with contract
10	WVT			g/(m^2·24h·0.1mm)	≤2.0	≤2.0	-